Effect of bleaching agent on the toughness of resin composites
Objective: To compare the fracture toughness (KIc) of resin composites on a four-point bending test and to assess the effect of distilled water and a home bleaching agent on the resistance of the materials to fracture.Method: seventy-two bar-shaped specimens were prepared from three materials: Rok (SDI), Estelite (Tokuyama), and Vit-l-escence (Ultradent) and divided into three groups. Two groups were assigned as “control" and conditioned in distilled water at 37oC for 24 hours or 21 days, respectively. The specimens in the third group (treatment) were stored in distilled water for 21 days and bleached using Polanight (SDI) for 2 hours daily. For each material, a total of 24 disc-shaped specimens were prepared and after each time interval loaded in a four-point bending test using a universal testing machine with a crosshead speed of 0.5 mm/m. The maximum load to specimen failure was recorded and the KIc was calculated. Result: Statistical analysis using two-way ANOVA showed a significant relationship between materials and treatment (p< 0.05). Tukey’s test showed that after 24 hours of immersion in distilled water, KIc was not significantly different between materials; Rok revealed the highest value followed by Estelite and Vit-l-escence. The bleaching agent significantly decreased the KIc values of Estelite and Rok while it did not affect that of Vita-l-escence. Immersion in distilled water for all resin composites caused a significant decrease in KIc.Conclusion: The fracture toughness of the resin composites was affected by the bleaching agent and 21day immersion in distilled water.
Division: Australian/New Zealand Division Meeting
Meeting:2014 Australian/New Zealand Division Meeting (Brisbane, Australia) Location: Brisbane, Australia
Year: 2014 Final Presentation ID: Abstract Category|Abstract Category(s):Scientific Groups
Authors
Bagheri, Rafat
( Shiraz University of Medical Sciences, Shiraz, , Iran
)
Ghazvini Ferooz, Maryam
( Monash University, Vic, , Australia
)